Bacterial behavior on coated porous titanium substrates for biomedical applications
Garvi Higueras, María Dolores
Lebrato Martínez, Julián
Rodríguez-Ortiz, José Antonio
Lebrato Vázquez, Clara
Torres Hernández, Yadir
|Departamento||Universidad de Sevilla. Departamento de Ingeniería y Ciencia de los Materiales y del Transporte
Universidad de Sevilla. Departamento de Ingeniería Química y Ambiental
|Publicado en||Surface and Coatings Technology, 357, 896-902.|
|Tipo de documento||Artículo|
|Resumen||In this work, bacterial behavior on dense and porous titanium substrates is discussed. Porous titanium was fabricated by a space holder technique (using 50 vol%, NH4HCO3 with particle sizes between 250 and 355 μm). These substrates were coated by su...
In this work, bacterial behavior on dense and porous titanium substrates is discussed. Porous titanium was fabricated by a space holder technique (using 50 vol%, NH4HCO3 with particle sizes between 250 and 355 μm). These substrates were coated by sulfonated PEEK (termed SPEEK). Characterization of the porous substrate was carried out using the Archimedes Method, Image Analysis, and three-dimensional X-ray Micro-Computed Tomography (including total and interconnected porosity, equivalent diameter, and pore shape factor), as well as mechanical characterization (specifically stiffness and yield strength). A detailed study was performed here to investigate the influence of substrate porosity on the adhesion and proliferation of E. coli, MRSA, and P. aeruginosa (common causes of orthopedic device-associated infections). Bacterial colonization was examined in terms of the initial bacterial concentration, as well as bacterial adherence to and growth on the surface and inside the pores. Results suggest that fully dense titanium supported the least bacterial colonization, while the porous titanium promoted bacterial growth in the medium and inside the cavities. Furthermore, the SPEEK coating deposited onto the samples inhibited bacteria growth inside the porous materials. In this manner, this study showed for the first time that SPEEK could have potential antibacterial properties to offset the increase in bacteria growth commonly observed in porous materials.
|Cita||Domínguez Trujillo, C., Garvi Higueras, M.D., Salazar-Moya, A., Lebrato Martínez, J., Rodríguez-Ortiz, J.A., Lebrato Vázquez, C.,...,Beltrán Custodio, A.M. (2019). Bacterial behavior on coated porous titanium substrates for biomedical applications. Surface and Coatings Technology, 357, 896-902.|
|SCT-beltrán-2019-bacterial.pdf||818.3Kb||[PDF]||Este documento no está disponible a texto completo hasta el 2021-02-01. Para más información póngase en contacto con email@example.com|
DOI: 10.1016/j.surfcoat.2018.10.098Versión del editor: https://www.sciencedirect.com/science/article/pii/S0257897218312052