High temperature internal friction measurements of 3YTZP zirconia polycrystals. High temperature background and creep
Autor/es | Simas, P.
Castillo Rodríguez, Miguel Nó, M. L. De-Bernardi, S. Gómez García, Diego Domínguez Rodríguez, Arturo San Juan, J. |
Departamento | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Fecha de publicación | 2014 |
Fecha de depósito | 2017-05-23 |
Publicado en |
|
Resumen | This work focuses on the high-temperature mechanic properties of a 3. mol% yttria zirconia polycrystals (3YTZP), fabricated by hot-pressureless sintering. Systematic measurements of mechanical loss as a function of temperature ... This work focuses on the high-temperature mechanic properties of a 3. mol% yttria zirconia polycrystals (3YTZP), fabricated by hot-pressureless sintering. Systematic measurements of mechanical loss as a function of temperature and frequency were performed. An analytical method, based on the generalized Maxwell rheological model, has been used to analyze the high temperature internal friction background (HTB). This method has been previously applied to intermetallic compounds but never to ceramics, except in a preliminary study performed on fine grain and nano-crystalline zirconia. The HTB increases exponentially and its analysis provides an apparent activation enthalpy which correlates well with that obtained from creep experiments. This fact shows on the one hand the plausibility of applying the generalized Maxwell model to ceramics, and on the other hand indicates the possibility of using mechanical spectroscopy as a complementary helpful technique to investigate the high temperature deformation mechanism of materials. |
Agencias financiadoras | European Union (UE) |
Identificador del proyecto | CSD2009-00013 |
Cita | Simas, P., Castillo Rodríguez, M., Nó, M.L., De-Bernardi, S., Gómez García, D., Domínguez Rodríguez, A. y San Juan, J. (2014). High temperature internal friction measurements of 3YTZP zirconia polycrystals. High temperature background and creep. Journal of the European Ceramic Society, 34 (15), 1-11. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
High temperature internal ... | 98.28Kb | [PDF] | Ver/ | |