Artículo
Fluage de monocristaux de NiO
Autor/es | Cabrera Cano, J.
Domínguez Rodríguez, Arturo Márquez Delgado, Rafael Castaing, Jean |
Departamento | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Fecha de publicación | 1978 |
Fecha de depósito | 2015-09-04 |
Publicado en |
|
Resumen | NiO single crystals have been subjected to constant-load compressive creep along (100). Stresses between 50 MPa and 120 MPa and temperatures between 950 °C and 1 200 °C were studied. The activation energy observed suggests ... NiO single crystals have been subjected to constant-load compressive creep along (100). Stresses between 50 MPa and 120 MPa and temperatures between 950 °C and 1 200 °C were studied. The activation energy observed suggests that oxygen diffusion is the rate-controlling process. Des expériences de compression à charge constante, selon < 100 >, ont été réalisées sur des monocristaux de NiO. Les contraintes utilisées vont de 50 MPa à 120 MPa et les températures de 950 °C à 1200 °C. L'énergie ... Des expériences de compression à charge constante, selon < 100 >, ont été réalisées sur des monocristaux de NiO. Les contraintes utilisées vont de 50 MPa à 120 MPa et les températures de 950 °C à 1200 °C. L'énergie d'activation du fluage suggère que la diffusion de l'oxygène joue un rôle prédominant sur la cinétique de déformation plastique. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Fluage de Monocristaux de NiO.pdf | 310.0Kb | [PDF] | Ver/ | |