Fluage de monocristaux de NiO
Author/s | Cabrera Cano, J.
Domínguez Rodríguez, Arturo Márquez Delgado, Rafael Castaing, Jean |
Department | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Publication Date | 1978 |
Deposit Date | 2015-09-04 |
Published in |
|
Abstract | NiO single crystals have been subjected to constant-load compressive creep along (100). Stresses between 50 MPa and 120 MPa and temperatures between 950 °C and 1 200 °C were studied. The activation energy observed suggests ... NiO single crystals have been subjected to constant-load compressive creep along (100). Stresses between 50 MPa and 120 MPa and temperatures between 950 °C and 1 200 °C were studied. The activation energy observed suggests that oxygen diffusion is the rate-controlling process. Des expériences de compression à charge constante, selon < 100 >, ont été réalisées sur des monocristaux de NiO. Les contraintes utilisées vont de 50 MPa à 120 MPa et les températures de 950 °C à 1200 °C. L'énergie ... Des expériences de compression à charge constante, selon < 100 >, ont été réalisées sur des monocristaux de NiO. Les contraintes utilisées vont de 50 MPa à 120 MPa et les températures de 950 °C à 1200 °C. L'énergie d'activation du fluage suggère que la diffusion de l'oxygène joue un rôle prédominant sur la cinétique de déformation plastique. |
Files | Size | Format | View | Description |
---|---|---|---|---|
Fluage de Monocristaux de NiO.pdf | 310.0Kb | ![]() | View/ | |