Pure diffusional creep of NiO polycrystals
Author/s | Jiménez Melendo, Manuel
![]() ![]() ![]() ![]() ![]() ![]() Cabrera Cano, J. Domínguez Rodríguez, Arturo Castaing, Jules |
Department | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Date | 1983 |
Published in |
|
Abstract | Compressive creep testing of polycrystalline NiO has been performed in air and argon, at temperatures between 1 100 and 1 500 °C (0.61 to 0.79 TM) under loads corresponding to initial applied stresses from 6 to 90 MPa. ... Compressive creep testing of polycrystalline NiO has been performed in air and argon, at temperatures between 1 100 and 1 500 °C (0.61 to 0.79 TM) under loads corresponding to initial applied stresses from 6 to 90 MPa. Nabarro creep was observed in the lower stress range; creep rate and oxygen diffusivity show a good correlation. Des essais de fluage en compression ont été faits sur des polycristaux de NiO, dans l'air et l'argon, à des températures entre 1 100 et 1 500 °C (0,61 à 0,79 TF) sous des charges correspondant à des contraintes initiales ... Des essais de fluage en compression ont été faits sur des polycristaux de NiO, dans l'air et l'argon, à des températures entre 1 100 et 1 500 °C (0,61 à 0,79 TF) sous des charges correspondant à des contraintes initiales entre 6 et 90 MPa. Le fluage Nabarro a été observé à faible contrainte; la vitesse de déformation et la diffusivité de l'oxygène montrent une bonne corrélation. |
Files | Size | Format | View | Description |
---|---|---|---|---|
Pure diffusional.pdf | 460.2Kb | ![]() | View/ | |