dc.identifier.citation | Peñuela Ruiz, C. (2022). Influencia del proceso de encolado en la tenacidad a fractura interlaminar de uniones encoladas no simétricas composite-composite mediante el ensayo DCB. (Trabajo Fin de Grado Inédito). Universidad de Sevilla, Sevilla. | |
dc.identifier.uri | https://hdl.handle.net/11441/140141 | |
dc.description.abstract | El auge de los materiales compuestos en la industria aeronáutica, al igual que en otros sectores, ha dado pie a
realizar numerosas investigaciones. En concreto, se están realizando gran cantidad de estudios acerca de las
uniones encoladas debido a que estas están cobrando cada vez mayor importancia en esta industria, y, aunque
presentan ciertas ventajas frente a las uniones remachadas, que han sido empleadas tradicionalmente, aún
generan desconfianza. Evaluar, por lo tanto, la calidad de las uniones encoladas es un trabajo necesario para
poder extender su uso con seguridad. La evaluación de este tipo de uniones se lleva a cabo mediante la obtención
de la tenacidad a la fractura interlaminar, cuyos ensayos (DCB y CDP) están ampliamente recogidos en las
normas, aunque solo para casos simétricos.
Debido a la gran cantidad de uniones no simétricas encontradas en la industria y a que el proceso de curado es
un factor importante en de este tipo de uniones, se ha propuesto como objetivo de este proyecto, conocer la
influencia del proceso de curado en la tenacidad a la fractura interlaminar en probetas de ensayo no simétricas.
Para ello se ha llevado a cabo una campaña de ensayos Double Cantilever Beam (DCB) en la que se han
empleado probetas con distinto espesor en ambos adherentes y que han sido obtenidas mediante distintas
configuraciones de unión: co-encolado, co-curado y encolado secundario. Además, se ha estudiado el modo de
fallo de cada una de dichas probetas. | es |
dc.description.abstract | The rise of composite materials in the aeronautical industry, as in other sectors, has given rise to a great deal of
research. In particular, a large number of studies are being carried out on bonded joints because they are
becoming increasingly important in this industry and, although they have certain advantages over the riveted
joints that have traditionally been used, they still generate mistrust. Evaluating the quality of bonded joints is
therefore a necessary task in order to extend their use safely. The evaluation of this type of joints is carried out
by obtaining the interlaminar fracture toughness, whose tests (DCB and CDP) are widely included in the
standards, although only for symmetrical cases.
Due to the large number of non-symmetrical joints found in the industry and to the fact that the curing process
is an important factor in this type of joints, the objective of this project was to determine the influence of the
curing process on the interlaminar fracture toughness in non-symmetrical test specimens. For this purpose, a
Double Cantilever Beam (DCB) test campaign has been carried out using specimens with different thickness in
both adhesives and obtained by different bonding configurations: co-bonding, co-curing and secondary bonding.
In addition, the failure mode of each of these specimens has been studied. | es |
dc.format | application/pdf | es |
dc.format.extent | 76 p. | es |
dc.language.iso | spa | es |
dc.rights | Attribution-NonCommercial-NoDerivatives 4.0 Internacional | * |
dc.rights.uri | http://creativecommons.org/licenses/by-nc-nd/4.0/ | * |
dc.title | Influencia del proceso de encolado en la tenacidad a fractura interlaminar de uniones encoladas no simétricas composite-composite mediante el ensayo DCB | es |
dc.type | info:eu-repo/semantics/bachelorThesis | es |
dc.type.version | info:eu-repo/semantics/publishedVersion | es |
dc.rights.accessRights | info:eu-repo/semantics/openAccess | es |
dc.contributor.affiliation | Universidad de Sevilla. Departamento de Mecánica de Medios Continuos y Teoría de Estructuras | es |
dc.date.embargoEndDate | 2022 | |
dc.description.degree | Universidad de Sevilla. Grado en Ingeniería de las Tecnologías Industriales | es |