Effects of high temperature treatments in air and argon on the magnetic properties of HITPERM alloys
Autor/es | Blázquez Gámez, Javier Sebastián
Conde Amiano, Clara Francisca Conde Amiano, Alejandro Roth, Stefan Güth, Albert |
Departamento | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Fecha de publicación | 2006 |
Fecha de depósito | 2016-12-07 |
Publicado en |
|
Resumen | The oxidation behavior of FeCo(NbZr)B(Cu) alloy series was studied. After heating up to 1073 K, an oxide layer View the MathML source∼1μm thick with a two-layer structure can be identified previous to a sharp interface ... The oxidation behavior of FeCo(NbZr)B(Cu) alloy series was studied. After heating up to 1073 K, an oxide layer View the MathML source∼1μm thick with a two-layer structure can be identified previous to a sharp interface between the oxide layer and alloy matrix, where no oxygen is detected. The coercivity of nanocrystallized samples increases, independently of the gas environment, during additional long-time-annealing without a significant change of the microstructure |
Cita | Blázquez Gámez, J.S., Conde Amiano, C.F., Conde Amiano, A., Roth, S. y Güth, A. (2006). Effects of high temperature treatments in air and argon on the magnetic properties of HITPERM alloys. Journal of Magnetism and Magnetic Materials, 304 (2), 627-629. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Effects of high temperature.pdf | 1.003Mb | [PDF] | Ver/ | |