Artículo
Effect of partial substitution of Ge for B on the high temperature response of soft magnetic nanocrystalline alloys
Autor/es | Blázquez Gámez, Javier Sebastián
Roth, Stefan Conde Amiano, Alejandro |
Departamento | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Fecha de publicación | 2005 |
Fecha de depósito | 2016-12-07 |
Publicado en |
|
Resumen | The effect of partial substitution of Ge for B in Fe78Co5Zr6B10Cu1 alloy on the microstructure, crystallization process and magnetic properties of the amorphous and nanocrystalline alloys was studied. Special attention was ... The effect of partial substitution of Ge for B in Fe78Co5Zr6B10Cu1 alloy on the microstructure, crystallization process and magnetic properties of the amorphous and nanocrystalline alloys was studied. Special attention was focused on the saturation magnetization response at high temperature and its dependence on the microstructure. Although the Curie temperature of the amorphous phase is not affected by the partial substitution of Ge for B, the saturation magnetization increases ∼10% with respect to the alloy without Ge |
Cita | Blázquez Gámez, J.S., Roth, S. y Conde Amiano, A. (2005). Effect of partial substitution of Ge for B on the high temperature response of soft magnetic nanocrystalline alloys. Journal of Alloys and Compounds, 395 (1-2), 313-317. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Effect of Partial.pdf | 638.8Kb | [PDF] | Ver/ | |