Opened Access Creep of (La0.55Sr0.45)0.99Mn1-yGayO3
Estadísticas
Icon
Exportar a
Autor: Routbort, Jules
Ralph, James
Cook, R. E.
Clauss Klamp, Caroline María
Ramírez de Arellano López, Antonio
Departamento: Universidad de Sevilla. Departamento de Física de la Materia Condensada
Fecha: 2003
Publicado en: Physical Chemistry Chemical Physics: PCCP, 5, 2232–2236
Tipo de documento: Artículo
Resumen: Steady-state compressive creep was measured in (La0.55Sr0.45)0.99Mn1−yGayO3 at temperatures from 1200 to 1270 °C in air at stresses (σ) from 13 to 40 MPa. The Ga concentration was y = 0, 0.05, and 0.10. Strains to 0.14 were obtained. In the creep equation for strain rate, = An exp(−Q/RT), stress exponents (n) were between 1.3 and 1.7, indicating that diffusional flow is the dominant creep mechanism, and the activation energy (Q) was found to vary from 355 kJ mol−1 for y = 0 to 485 kJ mol−1 for y = 0.10.
Tamaño: 330.5Kb
Formato: PDF

URI: http://hdl.handle.net/11441/23380

Mostrar el registro completo del ítem


Esta obra está bajo una Licencia Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 Internacional

Este registro aparece en las siguientes colecciones