An investigation on the formation mechanism of nano ZrB2 powder by a magnesiothermic reaction
Autor/es | Jalaly, M.
Bafghi, M. Sh Tamizifar, M. Gotor Martínez, Francisco José |
Departamento | Universidad de Sevilla. Departamento de Química Inorgánica |
Fecha de publicación | 2014 |
Fecha de depósito | 2018-04-24 |
Publicado en |
|
Resumen | Nanocrystalline zirconium diboride (ZrB2) powder was produced by mechanochemistry from the magnesiothermic reduction in the Mg/ZrO 2/B2O3 system. The use of high-energy milling conditions was essential to induce a mechanically ... Nanocrystalline zirconium diboride (ZrB2) powder was produced by mechanochemistry from the magnesiothermic reduction in the Mg/ZrO 2/B2O3 system. The use of high-energy milling conditions was essential to induce a mechanically induced self-sustaining reaction (MSR) and significantly reduce the milling time required for complete conversion. Under these conditions, it was found that the ignition time for ZrB2 formation was only about a few minutes. In this study, the mechanism for the formation of ZrB2 in this system was determined by studying the relevant sub-reactions, the effect of stoichiometry, and the thermal behavior of the system. |
Agencias financiadoras | Gobierno de España |
Identificador del proyecto | No. MAT2011-22981 |
Cita | Jalaly, M., Bafghi, M.S., Tamizifar, M. y Gotor Martínez, F.J. (2014). An investigation on the formation mechanism of nano ZrB2 powder by a magnesiothermic reaction. Journal of Alloys and Compounds, 588, 36-41. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
An investigation on the formation ... | 797.0Kb | [PDF] | Ver/ | |