Effect of tantalum content on the microstructure and mechanical behavior of cermets based on (TixTa1-x)(C0.5N0.5) solid solutions

Abstract

Titanium-tantalum carbonitride, (Ti, Ta)(C, N), based cermets with different Ti and Ta contents were prepared using a mechanically induced self-sustaining reaction and then densified using a pressureless sintering process. Complete microstructural and mechanical characterizations were performed on the materials, which revealed that the size of the carbonitride ceramic particle was significantly reduced when the Ta content was increased. The flexural strength and fracture toughness were measured using the ball on three balls test and the indentation microfracture test, respectively. The strength profile was analyzed under the framework of Weibull theory. The change in the mechanical properties as a function of the Ta content was correlated with the normalized microstructural parameters, such as the binder mean free path. The decrease in toughness and flexural strength was attributed to the presence of intermetallic compounds in the binder phase, which was also corroborated by the nanoindentation tests.