Microstructure, elastic and inelastic properties of partially graphitized biomorphic carbons

Abstract

The microstructural characteristics and amplitude dependences of the Young's modulus E and internal friction (logarithmic decrement delta) of biocarbon matrices prepared by beech wood carbonization at temperatures T (carb) = 850-1600A degrees C in the presence of a nickel-containing catalyst have been studied. Using X-ray diffraction and electron microscopy, it has been shown that the use of a nickel catalyst during carbonization results in a partial graphitization of biocarbons at T (carb) a parts per thousand yen 1000A degrees C: the graphite phase is formed as 50- to 100-nm globules at T (carb) = 1000A degrees C and as 0.5- to 3.0-mu m globules at T (carb) = 1600A degrees C. It has been found that the measured dependences E(T (carb)) and delta(T (carb)) contain three characteristic ranges of variations in the Young's modulus and logarithmic decrement with a change in the carbonization temperature: E increases and delta decreases in the ranges T (carb) < 1000A degrees C and T (carb) > 1300A degrees C; in the range 1000 < T (carb) < 1300A degrees C, E sharply decreases and delta increases. The observed behavior of E(T (carb)) and delta(T (carb)) for biocarbons carbonized in the presence of nickel correlates with the evolution of their microstructure. The largest values of E are obtained for samples with T (carb) = 1000 and 1600A degrees C. However, the samples with T (carb) = 1600A degrees C exhibit a higher susceptibility to microplasticity due to the presence of a globular graphite phase that is significantly larger in size and total volume.