Ag+ release and corrosion behavior of zirconium carbonitride coatings with silver nanoparticles for biomedical devices
Autor/es | Calderon, V.S.
Escobar-Galindo, Ramón Oliveira, J.C. Cavaleiro, Albano Carvalho, Sandra |
Departamento | Universidad de Sevilla. Departamento de |
Fecha de publicación | 2013-05-15 |
Fecha de depósito | 2023-06-19 |
Publicado en |
|
Resumen | Zirconium carbonitride coatings with silver nanoparticles were produced by DC unbalanced dual magnetron sputtering system, using two targets, Zr and Zr/Ag in an Ar, C2H2 and N2 atmosphere. Stainless steel 316L and silicon ... Zirconium carbonitride coatings with silver nanoparticles were produced by DC unbalanced dual magnetron sputtering system, using two targets, Zr and Zr/Ag in an Ar, C2H2 and N2 atmosphere. Stainless steel 316L and silicon (100) substrates were used for electrochemical and structural characterization, respectively. Silver was found to be well distributed throughout the coatings, maintaining the films' composition in depth, while its diffusion to the electrolyte decreases as immersion time increases, stopping its release after 7 to 8 days of immersion. Electrochemical characterization revealed very stable films that have improved base material, without any diminished corrosion resistance due to the silver content. |
Agencias financiadoras | Ministerio de Ciencia e Innovación (MICIN). España |
Identificador del proyecto | CSD2008-00023 (CONSOLIDER-Ingenio 2010)
RyC2007-0026 |
Cita | Calderon, V.S., Escobar-Galindo, R., Oliveira, J.C., Cavaleiro, A. y Carvalho, S. (2013). Ag+ release and corrosion behavior of zirconium carbonitride coatings with silver nanoparticles for biomedical devices. Surface and Coatings Technology, 222, 104-111. https://doi.org/10.1016/j.surfcoat.2013.02.011. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
1-s2.0-S0257897213001667-main.pdf | 1.276Mb | [PDF] | Ver/ | |