Colombian metallurgical coke as catalysts support of the direct coal liquefaction
Autor/es | Rico, Diego
Agámez, Yazmin Romero, Eduard Centeno Gallego, Miguel Ángel Odriozola Gordon, Jose Antonio Díaz, José de Jesús |
Departamento | Universidad de Sevilla. Departamento de Química Inorgánica |
Fecha de publicación | 2019 |
Fecha de depósito | 2023-01-30 |
Publicado en |
|
Resumen | A Colombian metallurgical coke was modified in its surface chemistry and was used as support of iron sulfide catalysts for direct coal liquefaction. The modification was made by treatments with diluted oxygen and HNO3 at ... A Colombian metallurgical coke was modified in its surface chemistry and was used as support of iron sulfide catalysts for direct coal liquefaction. The modification was made by treatments with diluted oxygen and HNO3 at different conditions. Changes in surface chemistry were studied by determining the point of zero charge (PZC), the isoelectric point (IEP), thermogravimetric analysis (TGA), temperature programmed decomposition-mass spectrometry (TPD-MS), Diffuse-reflectance infrared Fourier transform spectroscopy (DRIFTS) and nitrogen adsorption at 77 K. The results show that the materials obtained have a wide range of functional groups incorporated in a different proportion and quantity. The textural parameters indicate that treatment with diluted oxygen increases the surface area and incorporates micropores while the samples treated with HNO3 maintain the textural properties of the original material. The catalysts were also characterized by Raman spectroscopy. It was found that impregnation with the iron sulfide precursor does not significantly affect the Raman characteristics of the support. Additionally, XRD analysis shows smaller pyrite crystallites in the coke enriched with oxygenated groups of phenol and lactone indicating better dispersion of the active phase. The amount of oxygen chemisorbed per gram of catalyst shows that both, oxygen and nitric acid treatments, improve the relative dispersion of the active phase. It was found that the presence of the catalysts increases the conversion and yields towards oils and gases with respect to those of the tests without catalysts. Cokes modified by dilute oxygen gaseous treatment contain surface phenol and lactone groups and present the highest yield to oils. |
Agencias financiadoras | Ministerio de Economía y Competitividad (MINECO). España |
Identificador del proyecto | ENE2017-82451-C3-3-R |
Cita | Rico, D., Agámez, Y., Romero, E., Centeno Gallego, M.Á., Odriozola Gordon, J.A. y Díaz, J.d.J. (2019). Colombian metallurgical coke as catalysts support of the direct coal liquefaction. Fuel, 255, 115748. https://doi.org/10.1016/j.fuel.2019.115748. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Colombian metallurgica.pdf | 4.808Mb | [PDF] | Ver/ | |