Development of a TiNbTaMoZr-Based High Entropy Alloy with Low Young´s Modulus by Mechanical Alloying Route
Autor/es | Normand, Juliette
Moriche Tirado, Rocío García Garrido, Cristina Sepúlveda Ferrer, Ranier Enrique Chicardi Augusto, Ernesto |
Departamento | Universidad de Sevilla. Departamento de Ingeniería y Ciencia de los Materiales y del Transporte Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Fecha de publicación | 2020-11 |
Fecha de depósito | 2022-02-10 |
Publicado en |
|
Resumen | In this work, an equiatomic TiNbTaMoZr-based high-entropy alloy (HEA) has been developed by a powder metallurgy route, which consists of a process of combined one-step low-temperature mechanical milling starting from the ... In this work, an equiatomic TiNbTaMoZr-based high-entropy alloy (HEA) has been developed by a powder metallurgy route, which consists of a process of combined one-step low-temperature mechanical milling starting from the transition metals as raw materials and a subsequent pressureless sintering. In this way, the optimized synthesized specimen, after 10 h of milling time, showed two di erent body-centered cubic (bcc) TiNbTaMoZr alloys, which, after sintering at 1450 C, 1 h of dwell time and a heating and cooling rate of 5 C min-1, it remained formed as two bcc TiNbTaMoZr-based HEAs. This material, with micrometric and equiaxed particles, and with homogeneously distributed phases, presented a Young’s modulus that was significantly higher (5.8 GPa) and lower (62.1 GPa) than that of the usual commercially pure (cp) Ti and Ti6Al4V alloy used for bone-replacement implants. It also presented similar values to those of the HEAs developed for the same purpose. These interesting properties would enable this TiNbTaMoZr-based HEA to be used as a potential biomaterial for bulk or porous bone implants with high hardness and low Young´s modulus, thereby preventing the appearance of stress-shielding phenomena |
Agencias financiadoras | Universidad de Sevilla |
Identificador del proyecto | 2019/00000600 |
Cita | Normand, J., Moriche Tirado, R., García Garrido, C., Sepúlveda Ferrer, R.E. y Chicardi Augusto, E. (2020). Development of a TiNbTaMoZr-Based High Entropy Alloy with Low Young´s Modulus by Mechanical Alloying Route. Metals, 10 (11). Article number 1463. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Development of a tinbtamozr-based ... | 8.827Mb | [PDF] | Ver/ | |