Plastic deformation of CoO has been performed at 4.2 K by compression of single crystals along <100>. The influence of thermodynamic conditions of specimen preparation has been shown. The dislocation structure observed by ...

Se ha estudiado por microscopía electrónica de transmisión la microestructura de deformación a altas temperaturas (1.300-1.550°C) de monocristales de Zr02-Y203 totalmente estabilizados. La variación observada en la ...

Vickers microhardness tests have been performed at room temperature on (100), (110), and (111) MgO faces for various orientations of the pyramid diagonal. The indentations may be deformed probably because of cracking. ...

Constant strain rate compressions along < 001 > have been performed on CoO single crystals (ε ∼ 6 x 10-5 s-1). Yield stresses and work hardening rates have been measured between 77 K and 1 400 K; CoO is very strong when ...

Des polycristaux de NiO de haute pureté ont été élaborés par frittage avec et sans charge. Ils ont été caractérisés par microscopie optique et électronique. Leur comportement en fluage a été étudié au dessus de 1200°C.

Compressive creep testing of polycrystalline NiO has been performed in air and argon, at temperatures between 1 100 and 1 500 °C (0.61 to 0.79 TM) under loads corresponding to initial applied stresses from 6 to 90 MPa. ...