Artículo
Enhancement of the Magnetic Refrigerant Capacity in Partially Amorphous Fe 70Zr 30 Powders Obtained by Mechanical Alloying
(Elsevier, 2012)
After mechanical alloying Fe 70Zr 30 composition from pure starting powders, an amorphous phase with Curie temperature T C = 244 K and an intermetallic compound (that should be non-stoichiometric Zr-rich fcc Fe 2Zr phase) ...
Artículo
Structure and magnetic properties of Fe–Nb–B amorphous/nanocrystalline alloys produced by compaction of mechanically alloyed powders
(AIP Publishing, 2010)
Mechanical alloying of Fe75Nb10B15 and Fe85Nb5B10 systems has been performed from an initial mixture of elemental powders. A bcc supersaturated solid solution is developed during milling for both alloys. However, Fe75Nb10B15 ...
Artículo
Joule heating as a technique for obtaining uncoupled soft and hard magnetic phases in a Finemet alloy
(AIP Publishing, 2007)
A detailed study on the microstructural evolution of the Fe73.9Cu0.9Nb3.1Si13.2B8.9 Finemet alloy upon Joule heating and its correlation with the magnetic properties is reported. Mössbauer spectroscopy suggests the ...
Artículo
Detection of the onset of nanocrystallization by calorimetric and magnetic measurements
(AIP Publishing, 2005-01-24)
It is generally accepted that measurements of the magnetic properties are more sensitive than measurements of the enthalpy changes in the detection of the onset of crystallization of ferromagnetic phases emerging from a ...
Artículo
Thermal and Microstructural Stability of the Soft Magnetic Fe60Co18Nb6B15Cu1 alloy
(Elsevier, 2007)
Temperature evolution of the coercivity of nanocrystalline samples of Fe60Co18Nb6B15Cu1 alloy with different crystalline fractions was measured from room temperature up to 690 K. Although room temperature coercivity increases ...
Artículo
Study of Phases Evolution in High-coercive MnAl Powders Obtained Through Short Milling Time of Gas-atomized Particles
(Elsevier, 2017)
Gas-atomized Mn54Al46 particles constituted nominally of only ε- and γ2-phases, i.e. no content of the ferromagnetic L10-type τ-phase, have been used to study the evolution of phases during short time of high-energy milling ...