Insolubilization and thermal stabilization of a long-chain polyester by noncatalyzed melt-polycondensation synthesis in air
Autor/es | Benítez Jiménez, José Jesús
Heredia Guerrero, José A. Barthel, Markus J Knicker, Heike E. Heredia, Antonio |
Fecha de publicación | 2017 |
Fecha de depósito | 2018-04-04 |
Publicado en |
|
Resumen | Self-standing films of poly(ω-hydroxyl hexadecanoic acid) [poly(ω-OHC16)] have been prepared by noncatalyzed melt-polycondensation in air at 150, 175, and 200 °C. Poly(ω-OHC16)s obtained are characterized as polyesters by ... Self-standing films of poly(ω-hydroxyl hexadecanoic acid) [poly(ω-OHC16)] have been prepared by noncatalyzed melt-polycondensation in air at 150, 175, and 200 °C. Poly(ω-OHC16)s obtained are characterized as polyesters by infrared spectroscopy (FT-IR) and solid state magic angle spinning 13C nuclear magnetic resonance (13C MAS-NMR). Structurally, poly(ω-OHC16)s are quite crystalline as revealed by wide angle X-ray diffraction (WAXD). The presence of oxygen in the reaction atmosphere causes a mild oxidation in the form of peroxyester species, tentatively at the interphase between poly(ω-OHC16) crystallites, and the structure amorphization. The interfacial peroxyester phase ends up in the encapsulation of the polyester grains and provides a barrier towards the action of solvents. Thermal stabilization and insolubility resulting from the synthesis conditions used are interesting features to prepare solvent and heat resistant poly(ω-OHC16) coatings. Thus, a few microns thick poly(ω-OHC16) layer has been fabricated on aluminum foil and its resistivity towards a chloroform:methanol (1:1, v:v) mixture has been confirmed |
Agencias financiadoras | Junta de Andalucía |
Cita | Benítez Jiménez, J.J., Heredia Guerrero, J.A., Barthel, M.J., Knicker, H.E. y Heredia, A. (2017). Insolubilization and thermal stabilization of a long-chain polyester by noncatalyzed melt-polycondensation synthesis in air. Journal of Applied Polymer Science, 134 (1), 1-31. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Insolubilization and thermal ... | 2.186Mb | [PDF] | Ver/ | |