Artículo
Evaluation of interfacial fracture toughness and friction coefficient in the single fiber fragmentation test
(Elsevier, 2011)
Single fiber fragmentation test is extensively employed to characterize the fiber-matrix interface in composites. A novel technique for evaluating fracture toughness and friction coefficient at the fiber-matrix interface ...
Artículo
Tensile and shear strength of bimaterial interfaces within composite materials
(Elsevier, 2016-03)
The determination of the tensile and shear strengths of homogeneous materials can be easily performed by standard tensile and shear (e.g. Iosipescu) tests. Nevertheless, when the determination of these strengths involves ...
Artículo
Unique real‐variable expressions of displacement and traction fundamental solutions covering all transversely isotropic elastic materials for 3D BEM
(Wiley, 2008)
A general, efficient and robust boundary element method (BEM) formulation for the numerical solution of 9 three-dimensional linear elastic problems in transversely isotropic solids is developed in the present work. The ...
Artículo
Fatigue crack initiation and damage characterization in Brazilian test specimens for adhesive joints
(Taylor & Francis, 2014)
The present study is focused on the fatigue failure initiation at bimaterial corners by means of a configuration based on the Brazilian disc specimens. These specimens were previously used for the generalized fracture ...
Artículo
Computing stress singularities in transversely isotropic multimaterial corners by means of explicit expressions of the orthonormalized Stroh-eigenvectors
(Elsevier, 2009-01)
Composite materials reinforced by unidirectional long fibers behave macroscopically as homogeneous transversely isotropic linear elastic materials. A general, accurate and computationally efficient procedure for the ...
Artículo
Representativity of the singular stress state in the failure of adhesively bonded joints between metals and composites
(Elsevier, 2009-09)
Several critical points, where both geometry and material properties change abruptly, arise in an adhesively bonded lap joint between a metallic and a composite material. These critical points, called multimaterial corners ...
Artículo
Effect of thermal residual stresses on matrix failure under transverse tension at micromechanical level: A numerical and experimental analysis
(Elsevier, 2011)
In the present work the influence at micromechanical scale of thermal residual stresses, originated in the cooling down associated to the curing process of fibrous composites, on inter-fibre failure under transverse tension ...
Artículo
A least squares procedure for the evaluation of multiple generalized stress intensity factors at 2D multimaterial corners by BEM
(Elsevier, 2012-03)
Detailed characterization of linear elastic stress states at corners and crack tips requires knowledge of the stress singularity orders, the characteristic angular functions and the generalized stress intensity factors ...
Artículo
Determination of Generalized Fracture Toughness in composite multimaterial closed corners with two singular terms - Part I: Test proposal and numerical analysis
(Elsevier, 2012-07)
In the present work a general procedure for the experimental evaluation of Generalized-Fracture-Toughness values at multimaterial closed corners is defined. The lack of symmetries in the stress fields at multimaterial ...
Artículo
Representativity of thermal stresses in designing composite joints based on singular stress states at multimaterial corners
(Elsevier, 2011-09)
Using adhesives curing at temperature in bonded joints between dissimilar materials (composites and metals) gives rise to residual stresses due to the difference in the value of the thermal expansion coefficients of the ...