Experimental observations of fatigue damage in cross-ply laminates using carbon/epoxy ultra-thin plies
(Elsevier, 2023-02-15)
The damage mechanisms of cross-ply laminates under fatigue loading have been deeply studied during last years. In the case of quasi-static loads the so-called scale effect has recently acquired renewed importance after the ...
Artículo
Numerical and experimental analysis of ultra-thin plies in carbon/epoxy cross-ply laminates subjected to bending after tensile cyclic loading
(Elsevier, 2023-12)
As a result of a fatigue testing campaign in cross-ply laminates with different thicknesses in the 90° ply block (conventional and ultra-thin), different cracking patterns were observed. While laminates with conventional ...
Artículo
Thermomechanical characterisation data of 30 g/m2 and 150 g/m2 cured unidirectional carbon/epoxy tape prepreg TP 402/T700S
(Elsevier, 2023)
With the aim to calculate through the Classical Laminate Theory the most reliable stress value generated in the 90° layer of cross-ply laminates tested under fatigue loading [1], the mechanical and thermal properties ...