Effect of stress and/or field annealing on the magnetic behavior of the „Co77Si13.5B9.5…90Fe7Nb3 amorphous alloy
Autor/es | Miguel, C.
Zhukov Egorova, Arkady Pavlovich Val, J.J del Ramírez de Arellano López, Antonio González, J. |
Departamento | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Fecha de publicación | 2005 |
Fecha de depósito | 2019-11-12 |
Publicado en |
|
Resumen | Variations of coercive field, induced magnetic anisotropy, and saturation magnetostriction constant
in sCo77Si13.5B9.5d90Fe7Nb3 amorphous ribbons submitted to stress and/or axial magnetic-field
annealing are reported. ... Variations of coercive field, induced magnetic anisotropy, and saturation magnetostriction constant in sCo77Si13.5B9.5d90Fe7Nb3 amorphous ribbons submitted to stress and/or axial magnetic-field annealing are reported. The annealing was carried out by using the Joule-heating effect saverage temperature values of the sample corresponding to the intensity of the electrical current were 273, 378, 409, and 445 °Cd and the applied stress and axial magnetic field during the thermal treatments were 500 MPa and 750 A/m, respectively. As a result of these treatments, a uniaxial in-plane magnetic anisotropy, which affects drastically the soft magnetic character of the samples, was developed. |
Identificador del proyecto | MAT2001-0082-C04-04 |
Cita | Miguel, C., Zhukov Egorova, A.P., Val, J.J.d., Ramírez de Arellano López, A. y González, J. (2005). Effect of stress and/or field annealing on the magnetic behavior of the „Co77Si13.5B9.5…90Fe7Nb3 amorphous alloy. Journal of Applied Physics, 97 (3), 034911. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
1.1845577.pdf | 701.7Kb | [PDF] | Ver/ | |