Formation mechanism of ZrB2-Al2O3 nanocomposite powder by mechanically induced self-sustaining reaction
Autor/es | Jalaly, M.
Bafghi, M. Sh Tamizifar, M. Gotor Martínez, Francisco José |
Departamento | Universidad de Sevilla. Departamento de Química Inorgánica |
Fecha de publicación | 2013 |
Fecha de depósito | 2018-04-19 |
Publicado en |
|
Resumen | ZrB2-Al2O3 nanocomposite powder was produced by aluminothermic reduction in Al/ZrO2/B2O 3 system. In this research, high energy ball milling was used to produce the necessary conditions to induce a mechanically induced ... ZrB2-Al2O3 nanocomposite powder was produced by aluminothermic reduction in Al/ZrO2/B2O 3 system. In this research, high energy ball milling was used to produce the necessary conditions to induce a mechanically induced self-sustaining reaction. The ignition time of the composite formation was found to be about 13 min. The synthesis mechanism in this system was investigated by examining the corresponding sub-reactions as well as changing the stoichiometry of reactants. Thermal behavior of the system was also studied. |
Agencias financiadoras | Gobierno de España |
Cita | Jalaly, M., Bafghi, M.S., Tamizifar, M. y Gotor Martínez, F.J. (2013). Formation mechanism of ZrB2-Al2O3 nanocomposite powder by mechanically induced self-sustaining reaction. Journal of Materials Science, 48, 7557-7567. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Formation mechanism of ZrB2–Al2O3 ... | 742.5Kb | [PDF] | Ver/ | |