Porous, robust highly conducting Ni-YSZ thin film anodes prepared by magnetron sputtering at oblique angles for application as anodes and buffer layers in solid oxide fuel cells
Autor/es | García García, Francisco Javier
Yubero Valencia, Francisco Rodríguez González-Elipe, Agustín Balomenou, Stella P. Tsiplakides, Dimitris Petrakopoulou, Ioanna Lambert, R. M. |
Fecha de publicación | 2015 |
Fecha de depósito | 2017-11-22 |
Publicado en |
|
Resumen | Uniform, highly porous, columnar thin films incorporating YSZ and NiO prepared by magnetron sputtering with deposition at glancing incidence exhibited stoichiometries close to that of the Y–Zr–Ni sputter target. Characterization ... Uniform, highly porous, columnar thin films incorporating YSZ and NiO prepared by magnetron sputtering with deposition at glancing incidence exhibited stoichiometries close to that of the Y–Zr–Ni sputter target. Characterization by means of SEM, XRD, XPS and RBS revealed that the uniformly distributed nickel component in the as-deposited films consisted of NiO, and that the YSZ component was essentially amorphous. Annealing such films at 850 °C in hydrogen resulted in crystallization of the YSZ phase with preservation of the columnar morphology, while the NiO underwent reduction to metallic Ni, which partially segregated to the film surface. The hydrogen-annealed thin film anodes exhibited high conductivity, comparable to that of conventionally-prepared anodes, in both hydrogen and hydrogen/water mixtures at temperatures relevant to SOFC operation. They were also robust against strain-induced separation from the substrate under limited thermal cycling in both oxidizing and reducing atmospheres and are promising candidates for use as anodes in their own right and as strain-accommodating buffer layers between conventional anodes and the electrolyte for use in SOFC applications. |
Identificador del proyecto | FP7/2007-2013
298300 MAT2013-40852R |
Cita | García García, F.J., Yubero Valencia, F., Rodríguez González Elipe, A., Balomenou, S.P., Tsiplakides, D., Petrakopoulou, I. y Lambert, R.M. (2015). Porous, robust highly conducting Ni-YSZ thin film anodes prepared by magnetron sputtering at oblique angles for application as anodes and buffer layers in solid oxide fuel cells. Journal of Hydrogen Energy, 40 (23), 7382-7387. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Porous, robust highly conducting ... | 819.0Kb | [PDF] | Ver/ | |