Physicochemical parameters - hydration performance relationship of the new endodontic cement MTA Repair HP
Autor/es | Jiménez Sánchez, María del Carmen
Segura Egea, Juan José Díaz Cuenca, Aranzazu |
Departamento | Universidad de Sevilla. Departamento de Estomatología |
Fecha de publicación | 2019-06-04 |
Fecha de depósito | 2024-09-11 |
Publicado en |
|
Resumen | Background: To characterize the chemical composition and textural parameters of the MTA Repair HP precursor
powder and their influence to hydration performance.
Material and Methods: Un-hydrated precursor material was ... Background: To characterize the chemical composition and textural parameters of the MTA Repair HP precursor powder and their influence to hydration performance. Material and Methods: Un-hydrated precursor material was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), X-ray fluorescence (XRF), laser diffraction (LD), N2 physisorption and field emission gun scanning electron microscopy (FEG-SEM). Setting time was assessed according to ASTM specification C 266. Hydrated material was analysed by XRD, FT-IR, energy dispersive X-ray (EDX) analysis and FEG-SEM. Results: Ca3 SiO5 and Ca2 SiO4 , in addition to CaWO4 as radiopacifier are the main compositional phases. Other measured parameters indicate high specific surface area of 4.8 m2 g-1, high aluminium content of 1.7 wt.% and low initial and final setting times of 12 and 199 min, respectively. Singular microstructural features consisting of high aspect ratio nanoparticles are main constituents of un-hydrated precursor. Besides, FEM-SEM observation shows notably growth of hexagonal shaped plate-like morphologies homogeneously distributed along the sample during hydration process. Conclusions: The short setting time measured for HP Repair, is correlated with high surface area of precursor powder, high Al content and the absence of compositional sulphate phases. |
Cita | Jiménez Sánchez, M.d.C., Segura Egea, J.J. y Díaz Cuenca, A. (2019). Physicochemical parameters - hydration performance relationship of the new endodontic cement MTA Repair HP. Journal of Clinical and Experimental Dentistry, 11 (8), e739-e744. https://doi.org/10.4317/jced.56013. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Physicochemical parameter - ... | 944.0Kb | [PDF] | Ver/ | |
Este registro aparece en las siguientes colecciones
Este documento está protegido por los derechos de propiedad intelectual e industrial. Sin perjuicio de las exenciones legales existentes, queda prohibida su reproducción, distribución, comunicación pública o transformación sin la autorización del titular de los derechos, a menos que se indique lo contrario.