Coordination chemistry of titanium and zinc in Ti(1−x)Zn2xO2 (0 ≤ x ≤ 1) ultrathin films grown by DC reactive magnetron sputtering
Autor/es | Caretti, Ignacio
Yuste, Miriam Torres, Ricardo Sánchez, Olga Jiménez Guerrero, Ignacio Escobar-Galindo, Ramón |
Departamento | Universidad de Sevilla. Departamento de Física Aplicada I |
Fecha de publicación | 2012 |
Fecha de depósito | 2023-06-20 |
Publicado en |
|
Resumen | XANES and RBS were used to explore the structural phase and composition transitions of ultrathin films with Ti(12x)Zn2xO2 stoichiometries, from very low (y0.5 at.%) to high (y25 at.%) titanium content. In this way, the ... XANES and RBS were used to explore the structural phase and composition transitions of ultrathin films with Ti(12x)Zn2xO2 stoichiometries, from very low (y0.5 at.%) to high (y25 at.%) titanium content. In this way, the coordination chemistry of Ti4+ and Zn2+ cations was examined for a wide range of oxide compositions |
Agencias financiadoras | Ministerio de Ciencia e Innovación (MICIN). España |
Identificador del proyecto | CSD2008-0023 (FUNCOAT)
MAT2010-21070-C02- 02 (MOCASIN) |
Cita | Caretti, I., Yuste, M., Torres, R., Sánchez, O., Jiménez Guerrero, I. y Escobar-Galindo, R. (2012). Coordination chemistry of titanium and zinc in Ti(1−x)Zn2xO2 (0 ≤ x ≤ 1) ultrathin films grown by DC reactive magnetron sputtering. RSC Advances, 2, 2696-2699. |