Numerical and experimental analysis of ultra-thin plies in carbon/epoxy cross-ply laminates subjected to bending after tensile cyclic loading
(Elsevier, 2023-12)
As a result of a fatigue testing campaign in cross-ply laminates with different thicknesses in the 90° ply block (conventional and ultra-thin), different cracking patterns were observed. While laminates with conventional ...
Artículo
Non-conventional failures caused by the edge effect in cross-ply laminates made of ultra-thin plies
(Elsevier, 2023)
In a fatigue testing programme of carbon/epoxy cross-ply laminates made of ultra-thin plies, non-conventional failures are observed. These non-conventional failures consist in longitudinal cracks in the 90◦ layer parallel ...
Artículo
Fatigue life of unidirectional 90° carbon/epoxy laminates made of conventional and ultra-thin plies varying manufacturing and testing conditions
(John Wiley & Sons Ltd., 2023)
Unidirectional 90° laminates (UD-90) have been tested under tension–tension loading (R = 0.1) to comprehend the effect of different conditions on their fatigue life. Four different case studies have been evaluated: the ...