Influence of a Novel Surface of Bioactive Implants on Osseointegration: A Comparative and Histomorfometric Correlation and Implant Stability Study in Minipigs
Autor/es | Romero Ruiz, Manuel María
Ríos-Santos, J.V. Ríos Carrasco, Blanca |
Departamento | Universidad de Sevilla. Departamento de Estomatología |
Fecha de publicación | 2019-05-09 |
Fecha de depósito | 2019-09-06 |
Publicado en |
|
Resumen | Purpose: The objective of this study was to assess the influence of a novel surface of dental implants (ContacTi®) on the osseointegration process in a minipig model. The surface was compared with other existing surfaces ... Purpose: The objective of this study was to assess the influence of a novel surface of dental implants (ContacTi®) on the osseointegration process in a minipig model. The surface was compared with other existing surfaces on the market (SLA® and SLActive®) by employing bone implant contact analysis (BIC) and implant stability. Method: Twelve minipigs were used with prior authorisation from an ethics committee. Three types of surfaces were tested: SLA® (sand-blasted acid-etched titanium), SLActive® (same but hydrophilic, performed under a nitrogen atmosphere), and ContacTi® (alumina particle bombardment of titanium, bioactivated when treated thermochemically) in 4.1 mm × 8 mm implants with internal connection and a polished neck. Twelve implants of each surface type (N = 36) were placed, sacrificing 1/3 of the animals at 2 weeks of placement, 1/3 at 4 weeks and the remaining 1/3 at 8 weeks. Numerical variables were compared with Analysis of Variance, and the correlation between ISQ and BIC was established with the Spearman’s rank correlation coefficient. Results: SLActive® and ContacTi® surfaces showed elevated osteoconductivity at 4 weeks, maintaining a similar evolution at 8 weeks (large amount of mature lamellar tissue with high maturity and bone quality). The SLA® surface showed slower maturation. The ISQ values in surgery were elevated (above 65), higher at necropsy and higher at 4 and 8 weeks in the SLA® group than in the other two (SLActive® and ContacTi®). No significant correlation was found between ISQ and BIC for each implant surface and necropsy time. Conclusion: The three surfaces analysed showed high RFA and BIC values, which were more favourable for the SLActive® and ContacTi® surfaces. No statistical correlation was found between the RFA and BIC values in any of the three surfaces analysed. |
Cita | Romero Ruiz, M.M., Ríos-Santos, J.V. y Ríos Carrasco, B. (2019). Influence of a Novel Surface of Bioactive Implants on Osseointegration: A Comparative and Histomorfometric Correlation and Implant Stability Study in Minipigs. International Journal of Molecular Sciences, 20 (9), 1-14. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
Influence of a Novel Surface.pdf | 1.621Mb | [PDF] | Ver/ | |
Este registro aparece en las siguientes colecciones
Excepto si se señala otra cosa, la licencia del ítem se describe como: Attribution-NonCommercial-NoDerivatives 4.0 Internacional
Items relacionados
Enseñando items relacionados por título, autor, creador y materia.
-
Artículo
Influence of implant design and under-preparation of the implant site on implant primary stability. An in vitro study
Herrero Climent, Mariano; Ferreira Lemos, Bernardo; Herrero Climent, Federico; Falcao, C.; Oliveira, Helder; Herrera Martínez, Manuela; Gil, Francisco Javier; Ríos Carrasco, Blanca; Ríos-Santos, J.V. (2020-06-20)The aim of this study was to evaluate the effects of different implant sites an under-preparation sequence associated with ...
-
Artículo
Effect of the Acid-Etching on Grit-Blasted Dental Implants to Improve Osseointegration: Histomorphometric Analysis of the Bone-Implant Contact in the Rabbit Tibia Model
Ríos Carrasco, Blanca; Lemos, Bernardo Ferreira; Herrero Climent, Mariano; Gil Mur, Javier; Ríos-Santos, J.V. (MDPI, 2021-11-22)Previous studies have shown that the most reliable way to evaluate the success of an implant is by bone-to-implant contact ...
-
Artículo
Design, processing and characterization of titanium with radial graded porosity for bone implants porosity for bone implants
Torres Hernández, Yadir; Trueba Muñoz, Paloma; Pavón, J.J.; Chicardi Augusto, Ernesto; Kamm, Paul H.; García-Moreno, Francisco; Rodríguez-Ortiz, José Antonio (Elsevier, 2016-07)Titanium cylinders with radial graded porosity, which are potentially suitable for biomedical applications (replacement ...