Influence of La and Ce additions on the magnetocaloric effect of Fe–B–Cr-based amorphous alloys
Autor/es | Law, Jia Yan
Franco García, Victorino Ramanujan, Raju Vijayaraghavan |
Departamento | Universidad de Sevilla. Departamento de Física de la Materia Condensada |
Fecha de publicación | 2011 |
Fecha de depósito | 2017-11-28 |
Publicado en |
|
Resumen | The magnetic entropy change (ΔSM), temperature of peak ΔSM (Tpk) and refrigerant capacity (RC) in Fe(RE)80B12Cr8 (RE = La, Ce, or Gd) alloys were studied. Increasing La, Ce, and Gd content led to relatively constant, ... The magnetic entropy change (ΔSM), temperature of peak ΔSM (Tpk) and refrigerant capacity (RC) in Fe(RE)80B12Cr8 (RE = La, Ce, or Gd) alloys were studied. Increasing La, Ce, and Gd content led to relatively constant, decrease, and increase in Tpk, respectively. Both the phenomenologically constructed universal curve for ΔSM and field dependence power laws demonstrated that these alloys exhibited similar critical exponents at Curie temperature. With 5% Ce added to Fe80B12Cr8, Tpk could be tuned near room temperature with relatively constant peak ΔSM. Fe79B12Cr8La1 exhibited enhanced RC compared to Gd5Si2Ge1.9Fe0.1. The tunable Tpk and enhanced RC are needed in active magnetic regenerators. |
Identificador del proyecto | AOARD-08-4018
MAT 2010-20537 FQM- 6462 N00014-11-1-0311 |
Cita | Law, J.Y., Franco García, V. y Ramanujan, R.V. (2011). Influence of La and Ce additions on the magnetocaloric effect of Fe–B–Cr-based amorphous alloys. Applied Physics Letters, 98 (19), 192503-1-192503-3. |
Ficheros | Tamaño | Formato | Ver | Descripción |
---|---|---|---|---|
64-2011 digital-2-4.pdf | 174.4Kb | [PDF] | Ver/ | |
Este registro aparece en las siguientes colecciones
Excepto si se señala otra cosa, la licencia del ítem se describe como: Attribution-NonCommercial-NoDerivatives 4.0 Internacional
Items relacionados
Enseñando items relacionados por título, autor, creador y materia.
-
Artículo
Amorphous Phase Formation and Heat Treating Evolution in Mechanically Alloyed Ti–Cu Alloy for Biomedical Applications
Urban, Petr; Astacio López, Raquel; Ternero Fernández, Fátima; Náhlík, L.; Cintas Físico, Jesús (Springer, 2022-07-27)The present work aims to produce TixCu100-x (x = 90, 80, 70, and 60) amorphous alloys by using high energy ball mill. The ...
-
Artículo
Mechanical alloying and amorphization of Ti75Cu25 alloy
Urban, Petr; Astacio López, Raquel; Aranda, R. M.; Ternero Fernández, Fátima; Cintas Físico, Jesús (Elsevier, 2022)Ti-Cu alloys are used in dental and medical applications, due to their good mechanical properties, corrosion resistance ...
-
Artículo
Mechanical Alloying as a Way to Produce Metastable Single-Phase High-Entropy Alloys beyond the Stability Criteria
Santiago Andrades, Lucía; Vidal Crespo, Antonio; Blázquez Gámez, Javier Sebastián; Ipus Bados, Jhon Jairo; Conde Amiano, Clara Francisca (MDPI, 2023-12)Various stability criteria developed for high-entropy alloys are applied to compositions produced by mechanical alloying. ...