The formation of ZnSe via a mechanically-induced self-sustaining reaction (MSR) from a Zn/Se mixture showed that only size reduction and mixing of the reactants without product formation occurred during the induction period ...

Monophase nanocrystalline powders belonging to the La 1-xSr xMnO 3±δ system (0≤x≤1) with a perovskite structure have been obtained by mechanochemistry synthesis using a planetary ball milling equipment from La 2O 3, SrO, ...

In this study we demonstrate the synthesis of quaternary semiconductor nanocrystals of stannite Cu2FeSnS4/rhodostannite Cu2FeSn3S8 (CFTS) via mechanochemical route using Cu, Fe, Sn and S elements as precursors in one-pot ...

The mechanochemical process denoted as a mechanically induced self-sustaining reaction was successfully applied in obtaining Mn-doped ZnS samples with Mn content between 0 and 5 mol%. The process consists in milling Zn/Mn/S ...

Cermets with a nominal composition (Ti 0.8Ta 0.2C 0.5N 0.5- 20 wt.% Co) were synthesised by a mechanically induced self-sustaining reaction (MSR) process from stoichiometric elemental powder blends. The MSR allowed the ...

Microstructure and mechanical characterization of (Ti,Ta)(C,N)-Co based solid solution cermets prepared by two mechanochemical synthesis processes (one- and two-step milling) and a pressureless sintering in protective ...

In this study, we demonstrate a one-pot mechanochemical synthesis of the nanocomposite composed of stannite Cu2FeSnS4 and rhodostannite Cu2FeSn3S8 nanocrystals using a planetary ball mill and elemental precursors (Cu, Fe, ...

Mechanosynthesis of La1-xSrxMnO3 (x = 0, 0.25, 0.5, 0.75 and 1) was carried out at room temperature from stoichiometric mixtures of La2O3, Mn2O3 and SrO, obtaining monophasic powders with the perovskite structure. Physical ...